Database Reference: NIST Structural Ceramics Database, SRD Database Number 30.
Journal Reference:
Elastic Moduli Data for Polycrystalline Ceramics, R. G. Munro, NISTIR 6853, (2002),Other Materials: Elastic Moduli Data
National Institute of Standards and Technology,
Gaithersburg, Maryland 20899.
Other Materials Properties: Property Data Summaries
Ref. Nbr. |
Exhibit Type |
Exhibit Number |
Value Type |
Measurement Method |
Matl. Nbr. |
T [°C] |
d [g/cm3] |
p [%] |
VL [km/s] |
VS [km/s] |
E [GPa] |
G [GPa] |
B [GPa] |
nu |
Table Notes |
---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
104 | Graph | 1 | x | sonic resonance | 23 | 0.072 | 141.4 | ||||||||
104 | Graph | 1 | x | sonic resonance | 23 | 0.076 | 136.5 | ||||||||
104 | Graph | 1 | x | sonic resonance | 23 | 0.095 | 132.4 | ||||||||
104 | Graph | 1 | x | sonic resonance | 23 | 0.09 | 130.3 | ||||||||
104 | Graph | 1 | x | sonic resonance | 23 | 0.133 | 116.5 | ||||||||
104 | Graph | 1 | x | sonic resonance | 23 | 0.133 | 112.4 | ||||||||
104 | Graph | 1 | x | sonic resonance | 23 | 0.192 | 86.9 | ||||||||
104 | Graph | 1 | x | sonic resonance | 23 | 0.195 | 84.1 | ||||||||
104 | Graph | 1 | x | sonic resonance | 23 | 0.325 | 46.2 | ||||||||
104 | Graph | 1 | x | sonic resonance | 23 | 0.325 | 42.1 | ||||||||
104 | Graph | 1 | x | sonic resonance | 23 | 0.349 | 29 | ||||||||
104 | Graph | 1 | x | sonic resonance | 23 | 0.363 | 14.5 | ||||||||
104 | Graph | 1 | x | sonic resonance | 23 | 0.365 | 12.4 | ||||||||
104 | Graph | 1 | x | sonic resonance | 23 | 0.38 | 12.4 | ||||||||
104 | Graph | 1 | x | sonic resonance | 23 | 0.38 | 7.6 | ||||||||
104 | Graph | 2 | x | sonic resonance | 17 | 5.192 | 19.1 | ||||||||
104 | Graph | 2 | x | sonic resonance | 66 | 5.192 | 19.1 | ||||||||
104 | Graph | 2 | x | sonic resonance | 80 | 5.192 | 19.1 | ||||||||
104 | Graph | 2 | x | sonic resonance | 120 | 5.192 | 19 | ||||||||
104 | Graph | 2 | x | sonic resonance | 174 | 5.192 | 18.9 | ||||||||
104 | Graph | 2 | x | sonic resonance | 212 | 5.192 | 18.8 | ||||||||
104 | Graph | 2 | x | sonic resonance | 261 | 5.192 | 18.7 | ||||||||
104 | Graph | 2 | x | sonic resonance | 252 | 5.192 | 18.6 | ||||||||
104 | Graph | 2 | x | sonic resonance | 311 | 5.192 | 18.6 | ||||||||
104 | Graph | 2 | x | sonic resonance | 345 | 5.192 | 18.5 | ||||||||
104 | Graph | 2 | x | sonic resonance | 394 | 5.192 | 18.4 | ||||||||
104 | Graph | 2 | x | sonic resonance | 428 | 5.192 | 18.3 | ||||||||
104 | Graph | 2 | x | sonic resonance | 472 | 5.192 | 18.2 | ||||||||
104 | Graph | 2 | x | sonic resonance | 516 | 5.192 | 18.1 | ||||||||
104 | Graph | 2 | x | sonic resonance | 565 | 5.192 | 18 | ||||||||
104 | Graph | 2 | x | sonic resonance | 599 | 5.192 | 17.9 | ||||||||
104 | Graph | 2 | x | sonic resonance | 633 | 5.192 | 17.8 | ||||||||
104 | Graph | 2 | x | sonic resonance | 669 | 5.192 | 17.7 | ||||||||
104 | Graph | 2 | x | sonic resonance | 697 | 5.192 | 17.7 | ||||||||
104 | Graph | 2 | x | sonic resonance | 806 | 5.192 | 17.5 | ||||||||
104 | Graph | 2 | x | sonic resonance | 834 | 5.192 | 17.4 | ||||||||
104 | Graph | 2 | x | sonic resonance | 884 | 5.192 | 17.1 | ||||||||
104 | Graph | 2 | x | sonic resonance | 884 | 5.192 | 17 | ||||||||
104 | Graph | 2 | x | sonic resonance | 889 | 5.192 | 16.9 | ||||||||
104 | Graph | 2 | x | sonic resonance | 913 | 5.192 | 16.8 | ||||||||
104 | Graph | 2 | x | sonic resonance | 1045 | 5.192 | 15.9 | ||||||||
105 | Table | III | c | extrapolation | 23 | 0 | 169.1 | 64.4 | 150.62 | 0.313 | |||||
105 | Graph | 2 | x | sonic resonance | 23 | 0.029 | 153 | ||||||||
105 | Graph | 2 | x | sonic resonance | 23 | 0.03 | 153 | ||||||||
105 | Graph | 2 | x | sonic resonance | 23 | 0.033 | 151 | ||||||||
105 | Graph | 2 | x | sonic resonance | 23 | 0.038 | 153 | ||||||||
105 | Graph | 2 | x | sonic resonance | 23 | 0.052 | 143 | ||||||||
105 | Graph | 2 | x | sonic resonance | 23 | 0.058 | 143 | ||||||||
105 | Graph | 2 | x | sonic resonance | 23 | 0.068 | 136 | ||||||||
105 | Graph | 2 | x | sonic resonance | 23 | 0.077 | 132 | ||||||||
105 | Graph | 2 | x | sonic resonance | 23 | 0.09 | 126 | ||||||||
105 | Graph | 2 | x | sonic resonance | 23 | 0.097 | 126 | ||||||||
105 | Graph | 2 | x | sonic resonance | 23 | 0.114 | 119 | ||||||||
105 | Graph | 2 | x | sonic resonance | 23 | 0.123 | 122 | ||||||||
105 | Graph | 2 | x | sonic resonance | 23 | 0.148 | 109 | ||||||||
105 | Graph | 2 | x | sonic resonance | 23 | 0.167 | 104 | ||||||||
105 | Graph | 2 | x | sonic resonance | 23 | 0.175 | 105 | ||||||||
105 | Graph | 2 | x | sonic resonance | 23 | 0.181 | 100 | ||||||||
105 | Graph | 2 | x | sonic resonance | 23 | 0.189 | 100 | ||||||||
105 | Graph | 2 | x | sonic resonance | 23 | 0.03 | 60 | ||||||||
105 | Graph | 2 | x | sonic resonance | 23 | 0.032 | 60 | ||||||||
105 | Graph | 2 | x | sonic resonance | 23 | 0.035 | 57 | ||||||||
105 | Graph | 2 | x | sonic resonance | 23 | 0.038 | 59 | ||||||||
105 | Graph | 2 | x | sonic resonance | 23 | 0.053 | 55 | ||||||||
105 | Graph | 2 | x | sonic resonance | 23 | 0.058 | 55 | ||||||||
105 | Graph | 2 | x | sonic resonance | 23 | 0.061 | 55 | ||||||||
105 | Graph | 2 | x | sonic resonance | 23 | 0.067 | 52 | ||||||||
105 | Graph | 2 | x | sonic resonance | 23 | 0.068 | 53 | ||||||||
105 | Graph | 2 | x | sonic resonance | 23 | 0.068 | 51 | ||||||||
105 | Graph | 2 | x | sonic resonance | 23 | 0.079 | 51 | ||||||||
105 | Graph | 2 | x | sonic resonance | 23 | 0.09 | 49 | ||||||||
105 | Graph | 2 | x | sonic resonance | 23 | 0.097 | 48 | ||||||||
105 | Graph | 2 | x | sonic resonance | 23 | 0.114 | 45 | ||||||||
105 | Graph | 2 | x | sonic resonance | 23 | 0.12 | 47 | ||||||||
105 | Graph | 2 | x | sonic resonance | 23 | 0.148 | 43 | ||||||||
105 | Graph | 2 | x | sonic resonance | 23 | 0.168 | 40 | ||||||||
105 | Graph | 2 | x | sonic resonance | 23 | 0.174 | 41 | ||||||||
105 | Graph | 2 | x | sonic resonance | 23 | 0.183 | 40 | ||||||||
105 | Graph | 2 | x | sonic resonance | 23 | 0.189 | 40 | ||||||||
105 | Graph | 2 | x | sonic resonance | 23 | 0.192 | 40 |
Privacy Statement/Security Notice
Disclaimer | FOIA
NIST is an agency of the
U.S. Commerce Department
Date created: 24 October 2002
Last updated: 24 October 2002
Technical inquiries:
Ceramics Division
NIST, 100 Bureau Drive, Stop 8520, Gaithersburg, MD 20899-8520.
Phone (301) 975-6119
Fax (301) 975-5334
Ceramics website comments:
Ceramics Webmaster
General NIST inquiries:
Public Inquiries Unit:
Phone (301) 975-NIST (6478)
TTY (301) 975-8295